# Effects of high pressure on the physical properties of MgB2

Preprint · T. Prikhna, W. Gawalek, Ya. Savchuk, A. Soldatov, V. Sokolovsky, M. Eisterer, H. W. Weber, J. Noudem, M. Serga, V. Turkevich, M. Tompsic, V. Tkach, N. Danilenko, W. Goldacker, F. Karau, I. Fesenko, M. Rindfleisch, J. Dellith, M. Wendt, S. You, V. Meerovich, S. Dub, V. Moshchil, N. Sergienko, A. Kozyrev and 5 more

- Archive id: arxiv:1005.2092
- Published: 2010-05-12
- arXiv: https://arxiv.org/abs/1005.2092
- Source URL: https://arxiv.org/abs/1005.2092
- PDF: https://arxiv.org/pdf/1005.2092
- Provenance: arxiv

## Abstract

The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and mechanical characteristics: critical current densities of 1.8-1.0 \\cdot 106 A/cm2 in the self field and 103 A/cm2 in a magnetic field of 8 T at 20 K, 5-3 \\cdot 105 A/cm2 in self field at 30 K, the corresponding critical fields being HC2 = 15 T at 22 K and irreversible fields Hirr =13 T at 20 K, and Hirr =3.5 T at 30 K, thermal conduction of 53+/-2 W/(m \\cdot κ), the Vickers hardness Hv=10.12+/-0.2 GPa under a load of 148.8 N and the fracture toughness K1C = 7.6+/-2.0 MPa m0.5 under the same load, the Young modulus E=213 GPa. Estimation of quenching current and AC losses allowed the conclusion that highpressure-prepared materials are promising for application in transformer-type fault current limiters working at 20-30 K.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---