# A Path to Higher Q0 with Large Grain Niobium Cavities

Preprint · Pashupati Dhakal, Gianluigi Ciovati, Ganapati Rao Myneni

- Archive id: arxiv:1205.6736
- Published: 2012-05-30
- arXiv: https://arxiv.org/abs/1205.6736
- Source URL: https://arxiv.org/abs/1205.6736
- PDF: https://arxiv.org/pdf/1205.6736
- Provenance: arxiv

## Abstract

The improvement of the quality factor Q0 of superconducting radio-frequency (SRF) cavities at medium accelerating gradients (20-25 MV/m) is important in order to reduce the cryogenic losses in continuous wave (CW) accelerators used for a variety of applications. In recent years, SRF cavities fabricated from ingot niobium have become a viable alternative to standard high-purity fine-grain Nb for the fabrication of high-performing SRF cavities with the possibility of significant cost reduction. Recent studies demonstrated the improvement of Q0 at medium field in cavities heat treated at 800-1200 °C without subsequent chemical etching \[ \]. To further explore this treatment procedure, a new induction furnace with an all-niobium hot-zone was commissioned \[ \]. A single-cell 1.5 GHz cavity fabricated from ingot material from CBMM, Brazil, with RRR 200, was heat treated in the new furnace in the temperature range 800-1400 °C for several hours. Residual resistance value of 1 - 5 nΩhave been consistently achieved on this cavity Q0-values as high as 4.6\\times1010 at 90 mT peak surface magnetic field at 2 K. Q0 values of about ~2\\times1011 have been measured at 1.5 K.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---
Space Kitty Archive · https://space-kitty.com · API: https://space-kitty.com/api/v1 · MCP: https://space-kitty.com/mcp · Premium: $0.20/request via x402 (Base Sepolia (testnet)). Metadata: arXiv (CC0), OpenAlex (CC0), Europe PMC (CC BY/CC0 works), ClinicalTrials.gov.