# Stabilization of high-Tc phase of BiS2-based superconductor LaO0.5F0.5BiS2 using high-pressure synthesis

Preprint · Yoshikazu Mizuguchi, Takafumi Hiroi, Joe Kajitani, Hiroshi Takatsu, Hiroaki Kadowaki, Osuke Miura

- Archive id: arxiv:1402.5189
- Published: 2014-02-21
- Venue: J. Phys. Soc. Jpn. 83 (2014) 053704
- DOI: https://doi.org/10.7566/jpsj.83.053704
- arXiv: https://arxiv.org/abs/1402.5189
- Source URL: https://arxiv.org/abs/1402.5189
- PDF: https://arxiv.org/pdf/1402.5189
- Provenance: arxiv

## Abstract

High-quality polycrystalline samples of LaO0.5F0.5BiS2 were obtained using high-pressure synthesis technique. The LaO0.5F0.5BiS2 sample prepared by heating at 700 C under 2 GPa showed superconductivity with superconducting transition temperatures (Tc) of Tconset = 11.1 and Tczero = 8.5 K in the electrical resistivity measurements and Tconset = 11.5 and Tcirr = 9.4 K in the magnetic susceptibility measurements, which are obviously higher than those of the LaO0.5F0.5BiS2 polycrystalline samples obtained using conventional solid-state reaction. It was found that the high-Tc phase can be stabilized under high pressure and relatively-low annealing temperature. X-ray diffraction analysis revealed that the high-Tc phase possessed a small ratio of lattice constants of a and c, c/a.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---