# Highly textured oxypnictide superconducting thin films on metal substrates

Preprint · Kazumasa Iida, Fritz Kurth, Masashi Chihara, Naoki Sumiya, Vadim Grinenko, Ataru Ichinose, Ichiro Tsukada, Jens Hänisch, Vladimir Matias, Takafumi Hatano, Bernhard Holzapfel, Hiroshi Ikuta

- Archive id: arxiv:1410.8743
- Published: 2014-10-31
- Venue: Appl. Phys. Lett. 105, 172602 (2014)
- DOI: https://doi.org/10.1063/1.4900931
- arXiv: https://arxiv.org/abs/1410.8743
- Source URL: https://arxiv.org/abs/1410.8743
- PDF: https://arxiv.org/pdf/1410.8743
- Provenance: arxiv

## Abstract

Highly textured NdFeAs(O,F) thin films have been grown on ion beam assisted deposition (IBAD)-MgO/Y2O3/Hastelloy substrates by molecular beam epitaxy. The oxypnictide coated conductors showed a superconducting transition temperature (Tc) of 43 K with a self-field critical current density (Jc) of 7.0 x 104 A/cm2 at 5 K, more than 20 times higher than powder-in-tube processed SmFeAs(O,F) wires. Albeit higher Tc as well as better crystalline quality than Co-doped BaFe2As2 coated conductors, in-field Jc of NdFeAs(O,F) was lower than that of Co-doped BaFe2As2. These results suggest that grain boundaries in oxypnictides reduce Jc significantly compared to that in Co-doped BaFe2As2 and, hence biaxial texture is necessary for high Jc.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---