# Enhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries

Preprint · Hikaru Sato, Hidenori Hiramatsu, Toshio Kamiya, Hideo Hosono

- Archive id: arxiv:1606.01477
- Published: 2016-06-05
- Venue: Sci. Rep. 6, 36828 (2016)
- DOI: https://doi.org/10.1038/srep36828
- arXiv: https://arxiv.org/abs/1606.01477
- Source URL: https://arxiv.org/abs/1606.01477
- PDF: https://arxiv.org/pdf/1606.01477
- Provenance: arxiv

## Abstract

Thin films of the iron-based superconductor BaFe2(As1-xPx)2 (Ba122:P) were fabricated on polycrystalline metal-tape substrates with two kinds of in-plane grain boundary alignments (well aligned (4 deg.) and poorly aligned (8 deg.)) by pulsed laser deposition. The poorly aligned substrate is not applicable to cuprate-coated conductors because the in-plane alignment \>4 deg. results in exponential decay of the critical current density (Jc). The Ba122:P film exhibited higher Jc at 4 K when grown on the poorly aligned substrate than on the well-aligned substrate even though the crystallinity was poorer. It was revealed that the misorientation angles of the poorly aligned samples were less than 6 deg., which are less than the critical angle of an iron-based superconductor, cobalt-doped BaFe2As2 (~9 deg.), and the observed strong pinning in the Ba122:P is attributed to the high-density grain boundaries with the misorientation angles smaller than the critical angle. This result reveals a distinct advantage over cuprate-coated conductors because well-aligned metal-tape substrates are not necessary for practical applications of the iron-based superconductors.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---