# Modeling of internal mechanical failure of all-solid-state batteries during electrochemical cycling, and implications for battery design

Article · Giovanna Bucci, Tushar Swamy, Yet-Ming Chiang, W. Craig Carter

- Archive id: arxiv:1703.00113
- Published: 2017-03-01
- Venue: Journal of Materials Chemistry A
- DOI: https://doi.org/10.1039/c7ta03199h
- arXiv: https://arxiv.org/abs/1703.00113
- Citations: 283
- Source URL: https://arxiv.org/abs/1703.00113
- PDF: https://arxiv.org/pdf/1703.00113
- Provenance: arxiv

## Abstract

This is the first quantitative analysis of mechanical reliability of all-solid state batteries. Mechanical degradation of the solid electrolyte (SE) is caused by intercalation-induced expansion of the electrode particles, within the constrain of a dense microstructure. A coupled electro-chemo-mechanical model was implemented to quantify the material properties that cause a SE to fracture. The treatment of microstructural details is essential to the understanding of stress-localization phenomena and fracture. A cohesive zone model is employed to simulate the evolution of damage. In the numerical tests, fracture is prevented only if electrode-particle's expansion is lower than 7.5% and the solid-electrolyte's fracture energy higher than $G\_c = 4$ J m$^{-2}$. Perhaps counter-intuitively, the analyses show that compliant solid electrolytes (with Young's modulus in the order of E$\_{SE} = 15$ GPa) are more prone to micro-cracking. This result, captured by our non-linear kinematics model, contradicts the speculations that sulfide SEs are more suitable for the design of bulk-type batteries than oxide SEs. Mechanical degradation is linked to the battery power-density. Fracture in solid Li-ion conductors represents a barrier for Li transport, and accelerates the decay of rate performance.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._