# Effect of mixed pinning landscapes produced by 6 MeV Oxygen irradiation on the resulting critical current densities J$_c$ in 1.3 $μ$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductors grown by co-evaporation

Preprint · N. Haberkorn, S. Suárez, P. D. Pérez, H. Troiani, P. Granell, F. Golmar, Jae-Hun Lee, S. H. Moon

- Archive id: arxiv:1706.04228
- Published: 2017-06-13
- Venue: Physica C 542 (2017) 6
- DOI: https://doi.org/10.1016/j.physc.2017.08.007
- arXiv: https://arxiv.org/abs/1706.04228
- Source URL: https://arxiv.org/abs/1706.04228
- PDF: https://arxiv.org/pdf/1706.04228
- Provenance: arxiv

## Abstract

We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$\_c$ and flux creep rates in 1.3 $μ$m thick GdBa$\_2$Cu$\_3$O$\_{7-d}$ coated conductor produced by co-evaporation. Pristine films with pinning produced mainly by random nanoparticles with diameter close to 50 nm were irradiated with doses between 2x10$^{13}$ cm$^{-2}$ and 4x10$^{14}$ cm$^{-2}$. At temperatures below 40 K with the magnetic field applied parallel (H//c) and at 45° (H//45°) to the c-axis, the in-field J$\_c$ dependences can be significantly improved by irradiation. For doses of 1x10$^{14}$ cm$^{-2}$ the J$\_c$ values at $μ$$\_0$H = 5 T are doubled without affecting significantly the J$\_c$ at small fields. Analyzing the flux creep rates as function of the temperature in both magnetic field configurations, it can be observed that the irradiation suppresses the peak associated with double-kink relaxation and increases the flux creep rates at intermediate and high temperatures. Under 0.5 T, the flux relaxation for H//c and H//45° in pristine films presents characteristic glassy exponents $μ$ = 1.63 and $μ$ = 1.45, respectively. For samples irradiated with 1x10$^{14}$ cm$^{-2}$, these values drop to $μ$ = 1.45 and $μ$ =1.24, respectively.