# First performance test of 30 mm iron-based superconductor single pancake coil under 24 T background field

Preprint · Dongliang Wang, Zhan Zhang, Xianping Zhang, Donghui Jiang, Chiheng Dong, He Huang, Wenge Chen, Qingjin Xu, Yanwei Ma

- Archive id: arxiv:1903.07960
- Published: 2019-03-19
- Venue: Supercond. Sci. Technol. 32 (2019) 04LT01
- DOI: https://doi.org/10.1088/1361-6668/ab09a4
- arXiv: https://arxiv.org/abs/1903.07960
- Source URL: https://arxiv.org/abs/1903.07960
- PDF: https://arxiv.org/pdf/1903.07960
- Provenance: arxiv

## Abstract

The iron-based superconductor (IBS) single pancake coil (SPC) with 30 mm inner diameter was firstly fabricated and tested under 24 T background field. This SPC was successfully made using the 7-filamentary Ba1-xKxFe2As2 (Ba122) tape by wind-and-react method. This IBS coil show the highest Ic value at magnetic field reported so far. For example, the transport critical current of this Ba122 SPC achieved 35 A at 4.2 K and 10 T, which is about half of that of short sample. This indicates that the non-insulation winding process together with the stainless-steel tape is suitable to the iron-based superconductor. Even more encouraging is the fact that the Ic of this SPC is still as high as 26 A under 24 T background field, which is still about 40% of that at zero external magnetic field. These results clearly demonstrate that the iron-based superconductors are very promising for high-field magnet applications.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---