# $\mathrm{La}_{\mathrm{1-}x} \mathrm{Mn}_{\mathrm{1-}y} \mathrm{O}_{\mathrm{1\pm}δ}$ buffer layers on inclined substrate deposited MgO templates for coated conductors

Preprint · Oleksiy Troshyn, Christian Hoffmann, Veit Große, Jens Hänisch, Lucas Becker, Rudolf Gross

- Archive id: arxiv:2012.01318
- Published: 2020-12-02
- arXiv: https://arxiv.org/abs/2012.01318
- Source URL: https://arxiv.org/abs/2012.01318
- PDF: https://arxiv.org/pdf/2012.01318
- Provenance: arxiv

## Abstract

Most commercial high-temperature superconducting coated conductors based on ion beam assisted MgO deposited templates use $\\mathrm{LaMnO\_3}$ (LMO) films as the terminating buffer layer. In contrast, coated conductors based on inclined substrate deposition (ISD)-MgO technology are still produced with homoepitaxial (homoepi)-MgO as the cap layer. In this work we report on the deposition of LMO buffer layers on ISD-MgO/homoepi-MgO by electron beam physical vapor deposition. The growth parameters of textured LMO films were studied systematically and their properties were optimized regarding the critical current densitiy ($J\_\\mathrm{c}$) of the subsequently deposited $\\mathrm{DyBa\_2Cu\_3O}\_{\\mathrm{7-}δ}$ (DyBCO) superconducting films. LMO films without outgrowths at the surface were obtained at growth rates of up to $4\\,\\mathrm{Å/s}$. Despite the formation of non-stoichiometric LMO films containing $59\\,\\%$ La, single-phase films were obtained at substrate temperatures below $775^{\\circ}\\mathrm{C}$ and at oxygen partial pressures of up to $4\\times10^{-4}\\,\\mathrm{mbar}$ due to a large homogeneity region towards La. The $J\_\\mathrm{c}$ values of DyBCO films deposited on LMO were found to be independent of the LMO thickness in a range from $50\\,\\mathrm{nm}$ to $450\\,\\mathrm{nm}$. DyBCO films on LMO reach $J\_\\mathrm{c}=0.83\\,\\mathrm{MA/cm^2}$ at $77\\,\\mathrm{K}$ in zero applied field. This value is up to $30\\,\\%$ higher than those of DyBCO films grown directly on homoepi-MgO. The wide range of LMO growth parameters and higher $J\_\\mathrm{c}$ values of DyBCO on LMO compared to DyBCO on homoepi-MgO make this material attractive for its use in manufacturing coated conductors based on ISD-MgO technology.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---