# A15 Nb$_3$Si -- A "high" Tc superconductor synthesized at a pressure of one megabar and metastable at ambient conditions

Preprint · Jinhyuk Lim, J. S. Kim, Ajinkya C. Hire, Yundi Quan, R. G. Hennig, P. J. Hirschfeld, J. J. Hamlin, G. R. Stewart, Bart Olinger

- Archive id: arxiv:2012.02905
- Published: 2020-12-05
- Venue: Journal of Physics: Condensed Matter 33, 285705 (2021)
- DOI: https://doi.org/10.1088/1361-648x/abeace
- arXiv: https://arxiv.org/abs/2012.02905
- Source URL: https://arxiv.org/abs/2012.02905
- PDF: https://arxiv.org/pdf/2012.02905
- Provenance: arxiv

## Abstract

A15 Nb$\_3$Si is, until now, the only high temperature superconductor produced at high pressure (~110 GPa) that has been successfully brought back to room pressure conditions in a metastable condition. Based on the current great interest in trying to create metastable-at-room-pressure high temperature superconductors produced at high pressure, we have restudied explosively compressed A15 Nb$\_3$Si and its production from tetragonal Nb$\_3$Si. First, diamond anvil cell pressure measurements up to 88 GPa were performed on explosively compressed A15 Nb$\_3$Si material to trace Tc as a function of pressure. Tc is suppressed to ~ 5.2 K at 88 GPa. Then, using these Tc (P) data for A15 Nb$\_3$Si, pressures up to 92 GPa were applied at room temperature (which increased to 120 GPa at 5 K) on tetragonal Nb$\_3$Si. Measurements of the resistivity gave no indication of any A15 structure production, i.e., no indications of the superconductivity characteristic of A15 Nb$\_3$Si. This is in contrast to the explosive compression (up to P~110 GPa) of tetragonal Nb$\_3$Si, which produced 50-70% A15 material, Tc = 18 K at ambient pressure, in a 1981 Los Alamos National Laboratory experiment. Our theoretical calculations show that A15 Nb$\_3$Si has an enthalpy vs the tetragonal structure that is 0.07 eV/atom smaller at 100 GPa, implying that the accompanying high temperature (1000 deg C) caused by explosive compression is necessary to successfully drive the reaction kinetics of the tetragonal -\> A15 Nb$\_3$Si structural transformation. Annealing experiments on the A15 explosively compressed material reaching time scales of 39 years are consistent with this viewpoint.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---