# Electrochemical performance and diffusion kinetics of a NASICON type Na$_{3.3}$Mn$_{1.2}$Ti$_{0.75}$Mo$_{0.05}$(PO$_4$)$_3$/C cathode for low-cost sodium-ion batteries

Article · Madhav Sharma, Rajendra S. Dhaka

- Archive id: arxiv:2505.10572
- Published: 2025-05-13
- Venue: Small, 21, 2505200 (2025)
- DOI: https://doi.org/10.1002/smll.202505200
- arXiv: https://arxiv.org/abs/2505.10572
- Citations: 25
- Source URL: https://arxiv.org/abs/2505.10572
- PDF: https://arxiv.org/pdf/2505.10572
- Provenance: arxiv

## Abstract

We report the electrochemical performance and diffusion kinetics of a newly designed NASICON type Na$\_{3.3}$Mn$\_{1.2}$Ti$\_{0.75}$Mo$\_{0.05}$(PO$\_4$)$\_3$/C composite material as a cathode for cost-effective sodium-ion batteries. A novel strategy of small Mo doping successfully stabilizes the sample having high Mn content in single phase rhombohedral symmerty. The high-resolution microscopy analysis reveals nanocrystallites of around $\\sim$18 nm, uniformly embedded within the semi-graphitic carbon matrix, which enhances the surface electronic conductivity and effectively shortens the sodium-ion diffusion path. More importantly, we demonstrate a stable electrochemical behavior, with enhanced discharge capacity of 124 mAh/g at 0.1 C, having good reversibility and retaining 77\\% of its capacity after 300 cycles, and 70\\% even after 400 cycles at 2 C. The sodium-ion diffusion coefficients, estimated using both galvanostatic intermittent titration technique (GITT) and cyclic voltammetry are found to lie within the range of $10^{-9}$ to $10^{-11}$~cm$^2$/s. Additionally, the bond-valence site energy mapping predicted a sodium-ion migration energy barrier of 0.76 eV. A detailed distribution of relaxation times (DRT) analysis is used to deconvolute the electrochemical impedance spectra into distinct processes based on their characteristic relaxation times. Notably, the solid-state diffusion of sodium ions within the bulk electrode, with a relaxation time of $\\sim$50 s, shows a consistent trend with the diffusion coefficients obtained from GITT and Warburg-based evaluations across the state of charge.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

Topics: [Next-Generation Batteries](https://space-kitty.com/topics/next-gen-batteries)

---
Space Kitty Archive · https://space-kitty.com · API: https://space-kitty.com/api/v1 · MCP: https://space-kitty.com/mcp · Premium: $0.20/request via x402 (Base Sepolia (testnet)). Metadata: arXiv (CC0), OpenAlex (CC0), Europe PMC (CC BY/CC0 works), ClinicalTrials.gov.