# Investigating the Degradation of LATP Solid Electrolyte in High Alkaline Li-$O_2$ Batteries

Preprint · Tara P Mishra, Zhuohan Li, Meghan Shen, Maximilian Jaugstetter, Livia P Matte, Jung O. Park, Hyunjin Kim, Benjamin X Lam, Karen Bustillo, Gerbrand Ceder, Mary Scott

- Archive id: arxiv:2508.08654
- Published: 2025-08-12
- arXiv: https://arxiv.org/abs/2508.08654
- Citations: 1
- Source URL: https://arxiv.org/abs/2508.08654
- PDF: https://arxiv.org/pdf/2508.08654
- Provenance: arxiv

## Abstract

In this study, we address the challenge of electrolyte degradation in all-solid-state humidified Li-$O\_2$ batteries, which offer high theoretical energy density and potential cost advantages over conventional lithium-ion batteries. Combining STEM-EELS, and XPS characterizations with DFT calculations, we reveal the leaching of $(PO\_4)^{3+}$ and $Al^{3+}$ ions from the $Li\_{1.3}Al\_{0.3}Ti\_{1.7}(PO\_4)\_3$ (LATP) solid electrolyte upon battery discharge, caused by the highly alkaline environment. Upon charging, the leached ions precipitate as $Li\_3PO\_4$ and $AlPO\_4$, which accumulate on the LATP surface and contribute to battery degradation. A Ti-rich layer is observed at the surface after a few cycles due to depletion of other cations. Our findings suggest that the degradation products are formed through repeated dissolution and precipitation in the discharge-charge cycles. Furthermore, our results indicate that the Ti-rich layer on the LATP surface can potentially reduce parasitic reactions. Our study provides mechanistic understanding of LATP solid electrolyte degradation in humidified Li-$O\_2$ cell, paving the way for designing more durable and efficient Li-$O\_2$ batteries.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._