# High-pressure stabilization of Mg2IrH7: Structural proximity to high-Tc superconductivity

Preprint · Shubham Sinha, Wencheng Lu, Mads F. Hansen, Michael J. Hutcheon, Trevor W. Bontke, Lewis J. Conway, Kapildeb Dolui, Chris J. Pickard, Christoph Heil, Piotr A. Guńka, Stella Chariton, Vitali Prakapenka, Liangzi Deng, Ching-Wu Chu, Matthew N. Julian, Rohit P. Prasankumar, Timothy A. Strobel

- Archive id: arxiv:2602.23675
- Published: 2026-02-27
- arXiv: https://arxiv.org/abs/2602.23675
- Source URL: https://arxiv.org/abs/2602.23675
- PDF: https://arxiv.org/pdf/2602.23675
- Provenance: arxiv

## Abstract

Mg$\_2$IrH$\_6$ is a metastable complex metal hydride with a predicted superconducting transition temperature as high as 170 K at ambient pressure. Following the synthesis of isomorphic, insulating Mg$\_2$IrH$\_5$ at low pressure, higher-pressure studies were conducted to investigate the phase behavior and compound formation in this system. X-ray diffraction and Raman spectroscopic measurements indicate that cubic Mg$\_2$IrH$\_7$ is stabilized above ca. 40 GPa and coexists with a related hexagonal hydride with likely composition near Mg$\_2$IrH$\_5$. Electrical transport measurements show that the cubic Mg$\_2$IrH$\_7$ is insulating, in agreement with ab initio predictions, and persists during room-temperature decompression until $\\sim$20 GPa before reverting back to the cubic Mg$\_2$IrH$\_5$. The experimental results confirm ground-state structure predictions in the Mg-Ir-H system, and the formation of two nearly identical phases with surrounding compositions opens new opportunities to access superconducting Mg$\_2$IrH$\_6$ through non-equilibrium processing pathways.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---