# Stability Analysis of Superconductivity in $\textit{P6/mmm}$-LaSc$_2$H$_{24}$ and its Experimental Reproducibility from La-Sc Alloys

Preprint · Dmitrii V. Semenok, Ivan A. Troyan, Zhongyan Wu, Di Zhou, Emil A. Yuzbashyan, Boris L. Altshuler, Viktor V. Struzhkin

- Archive id: arxiv:2605.29985
- Published: 2026-05-28
- arXiv: https://arxiv.org/abs/2605.29985
- Source URL: https://arxiv.org/abs/2605.29985
- PDF: https://arxiv.org/pdf/2605.29985
- Provenance: arxiv

## Abstract

In this work, we analyze the feasibility of room-temperature superconductivity in the lanthanum-scandium hydride $\\textit{P6/mmm}$-LaSc$\_2$H$\_{24}$. We demonstrate that the electron-phonon coupling calculations performed using the $σ$-broadening of the double $δ$-function at the Fermi surface lead to a very strong dependence of $\\textit{T$\_c$}(σ)$ on the arbitrary $σ$, whereas the tetrahedral method for the electron-phonon interaction is free from this drawback and leads to $\\textit{T$\_c$}$ \> 300 K at 300 GPa in agreement with previous predictions. By analyzing the stability of the metallic state of LaSc$\_2$H$\_{24}$ at 250-300 GPa, we show that this compound is at the edge of the stability region ($ξ$ = 0.54), similar to $\\textit{fcc}$ LaH$\_{10}$ at 140-150 GPa. Seven experimental attempts to synthesize LaSc$\_2$H$\_{24}$ at 250-280 GPa starting from the (La,Sc$\_2$) alloy are unsuccessful and indicate the absence of even traces of superconductivity at 245-300 K in all the resulting La-Sc-H hydrides. The method for preparing the precursor by simultaneous deposition of La and Sc metals may be a key factor for the successful synthesis of LaSc$\_2$H$\_{24}$.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---