# Ni-Cr textured substrates with reduced ferromagnetism for coated conductor applications

Article · J. R. Thompson, A. Goyal, D. K. Christen, D. M. Kroeger

- Archive id: arxiv:cond-mat/0104239
- Published: 2001-04-12
- Venue: Physica C Superconductivity
- DOI: https://doi.org/10.1016/s0921-4534(01)00937-6
- arXiv: https://arxiv.org/abs/cond-mat/0104239
- Citations: 67
- Source URL: https://arxiv.org/abs/cond-mat/0104239
- PDF: https://arxiv.org/pdf/cond-mat/0104239
- Provenance: arxiv

## Abstract

A series of biaxially textured Ni(1-x)Cr(x) materials, with compositions x = 0, 7, 9, 11, and 13 at % Cr, have been studied for use as substrate materials in coated conductor applications with high temperature superconductors. The magnetic properties were investigated, including the hysteretic loss in a Ni-7 at % Cr sample that was controllably deformed; for comparison, the loss was also measured in a similarly deformed pure Ni substrate. Complementary X-ray diffraction studies show that thermo-mechanical processing produces nearly complete {100}\<100\> cube texturing, as desired for applications.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

Topics: [Applied Superconductivity & HTS Magnets](https://space-kitty.com/topics/applied-superconductivity)

---
Space Kitty Archive · https://space-kitty.com · API: https://space-kitty.com/api/v1 · MCP: https://space-kitty.com/mcp · Premium: $0.20/request via x402 (Base Sepolia (testnet)). Metadata: arXiv (CC0), OpenAlex (CC0), Europe PMC (CC BY/CC0 works), ClinicalTrials.gov.