# The high-pressure synthesis of MgB2

Preprint · T. A. Prikhna, W. Gawalek, A. B. Surzhenko, N. V. Sergienko, V. E. Moshchil, T. Habisreuther, V. S. Melnikov, S. N. Dub, P. A. Nagorny, M. Wendt, Ya. M. Savchuk, D. Litzkendorf, J. Dellith, S. Kracunovska, Ch. Schmidt

- Archive id: arxiv:cond-mat/0109216
- Published: 2001-09-12
- arXiv: https://arxiv.org/abs/cond-mat/0109216
- Source URL: https://arxiv.org/abs/cond-mat/0109216
- PDF: https://arxiv.org/pdf/cond-mat/0109216
- Provenance: arxiv

## Abstract

The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be manufactured. By a short-term (1h) high-pressure (2GPa) synthesis from Mg and B we have obtained samples 2.4-2.5 g/cm3 in density, 12.1-15.6 GPa in microhardness (under 4.96 N load), 170-200 kA/cm2 at 10 K and 58-62 kA/cm2 at 20 K in critical current density at a magnetic field of 1T. Samples demonstrated 8.5 T irreversible field at 10 K and 5.5 T at 20 K. The Ta positive influence on SC properties of MgB2 has been observed.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---
Space Kitty Archive · https://space-kitty.com · API: https://space-kitty.com/api/v1 · MCP: https://space-kitty.com/mcp · Premium: $0.20/request via x402 (Base Sepolia (testnet)). Metadata: arXiv (CC0), OpenAlex (CC0), Europe PMC (CC BY/CC0 works), ClinicalTrials.gov.