# High-pressure synthesis of superconducting Nb{1-x}B2 (x = 0-0.48) with the maximum Tc = 9.2 K

Preprint · A. Yamamoto, C. Takao, T. Masui, M. Izumi, S. Tajima

- Archive id: arxiv:cond-mat/0208331
- Published: 2002-08-16
- DOI: https://doi.org/10.1016/s0921-4534(02)01996-2
- arXiv: https://arxiv.org/abs/cond-mat/0208331
- Source URL: https://arxiv.org/abs/cond-mat/0208331
- PDF: https://arxiv.org/pdf/cond-mat/0208331
- Provenance: arxiv

## Abstract

Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and the lattice parameters also changed abruptly at x = 0.04. As x increased, the transition temperature Tc slightly rose and fell with the maximum value of 9.2 K at x = 0.24 for the samples sintered at 5 GPa and 1200 C. The Tc-value changed in the range from 7 K to 9 K, depending on the sintering pressure. A series of Ta1-xB2 (0 =\< x =\< 0.24) was also synthesized under high pressure to examine a special effect of high-pressure synthesis.

_Abstract reproduced under CC0-1.0 (arXiv descriptive metadata)._

---