Hydrogen in layered iron arsenides: Indirect electron doping to induce superconductivity

Abstract

Utilizing the high stability of calcium and rare earth hydrides, CaFeAsF1-xHx (x = 0.0-1.0) and SmFeAsO1-xHx (x = 0.0-0.47) have been first synthesized using high pressure to form hydrogen-substituted 1111 type iron-arsenide superconductors. Neutron diffraction and density functional calculations have demonstrated that the hydrogens are incorporated as H- ions occupying F- sites in the blocking layer of CaFeAsF. The resulting CaFeAsF1-xHx is non-superconducting, whereas SmFeAsO1-xHx is a superconductor, with an optimal Tc = 55 K at x 0.2. It was found that up to 40% of the O2- ions can be replaced by H- ions, with electrons being supplied into the FeAs-layer to maintain neutrality (O2- = H-+ e-). When x exceeded 0.2, Tc was reduced corresponding to an electron over-doped region.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.