Superconductivity and Rattling under High Pressure in the beta-Pyrochlore Oxide RbOs2O6

Abstract

Rattling-induced superconductivity in the beta-pyrochlore oxide RbOs2O6 is investigated under high pressures up to 6 GPa. Resistivity measurements in a high-quality single crystal show that the superconducting transition temperature Tc increases gradually from 6.3 K at ambient pressure to 8.8 K at 3.5 GPa, surprisingly remains almost constant at 8.8 \pm 0.1 K in a wide pressure range between 3.5 (Po) and 4.8 GPa, and suddenly drops to 6.3 K at Ps = 4.9 GPa, followed by a gradual decrease with further pressure increase. Two anomalies in the temperature dependence of the normal-state resistivity are observed at Po < P < Ps and P > Ps, revealing the presence of two high-pressure phases corresponding to the changes in Tc. The rattling of the Rb ion inside a cage made of Os and O atoms may be slightly and seriously modified in these high-pressure phases that probably have cages of reduced symmetry, respectively, so that electron-rattler interactions that govern the superconducting and transport properties of beta-RbOs2O6 are significantly affected.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.