High-pressure effects on single crystals electron-doped r$_{2-x}$Ce$_{x}$CuO$_{4}$

Abstract

We present high pressure diamond anvil cell synchrotron X-ray, resistivity, and ac-susceptibility measurements on electron-doped cuprate Pr$_{2-x}$Ce$_{x}$CuO$_{4}$ to much higher pressures than previously reported. At 2.72 GPa between 88 and 98$%$ of the superconducting T$^\prime$ phase \cite{Tprime} of the optimally doped Pr$_{1.85}$Ce$_{0.15}$CuO$_{4}$ transforms into the insulating phase T. The T$_{c}$ of the remaining 2-12$%$ T$^\prime$ phase is suppressed continuously from 22 K to 18.5 K at about 14 GPa. Remarkably, the T$_{c}$ of the over doped Pr$_{1.83}$Ce$_{0.17}$CuO$_{4}$ remains practically unchanged even at 32 GPa. This behavior of the electron-doped cuprate contrasts with that of the hole-doped cuprate for which T$_{c}$ is first substantially enhanced with applied pressure.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.