AC Losses of Copper Stabilized Multifilament YBCO Coated Conductors

Abstract

We report the data on magnetization losses and critical current of multifilament copper stabilized coated conductors. Eight centimeters long samples of copper stabilized YBa2Cu3O7-x (YBCO) coated conductors manufactured commercially were subdivided into superconducting filaments by near-IR laser micromachining. The width of the superconducting stripes was varied from 0.2 mm to 0.04 mm. Some of the samples were striated leaving superconducting bridges for current sharing between the filaments. The AC losses were measured at different sweep rates of the magnetic field up to 14 T/s. We will present the results for the hysteresis and coupling losses and discuss the means to reduce the coupling loss by changing the processing parameters of micromachining and by post-ablation treatment.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.