Analysis of post wet chemistry heat treatment effects on Nb SRF surface resistance

Abstract

Most of the current research in superconducting radio frequency (SRF) cavities is focused on ways to reduce the construction and operating cost of SRF based accelerators as well as on the development of new or improved cavity processing techniques. The increase in quality factors is the result of the reduction of the surface resistance of the materials. A recent test on a 1.5 GHz single cell cavity made from ingot niobium of medium purity and heat treated at 1400 C in a ultra-high vacuum induction furnace resulted in a residual resistance of about 1nanoohm and a quality factor at 2.0 K increasing with field up to 5x10^10 at a peak magnetic field of 90 mT. In this contribution, we present some results on the investigation of the origin of the extended Q0-increase, obtained by multiple HF rinses, oxypolishing and heat treatment of all Nb cavities.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.