Abstract

We have investigated the pressure-induced phase transition and superconducting properties of niobium disulfide (NbS$_2$) based on the density functional theory. The structures of NbS$_2$ at pressures from 0 to 200 GPa were predicted using the multi-algorithm collaborative (MAC) structure prediction technique. The previously known 1$T$-, 2$H$-, and 3$R$-NbS$_2$ were successfully reproduced. In addition, many metastable structures which are potential to be synthesized were also discovered. Based on the enthalpy calculations, we found that at 26 GPa NbS$_2$ transits from the double-hexagonal (2$H$) structure to the tetragonal $I4/mmm$ structure with a $10.6\%$ volume reduction. The calculated elastic constants and phonon dispersion curves of $I4/mmm$-NbS$_2$ confirm its mechanical and dynamical stability at high pressure. More interestingly, the coordination number of Nb in $I4/mmm$ structure is eight which is larger than that in the traditional metal dichalcogenides, indicating a new type of bondings of Nb and S atoms. In the new Nb-S bondings, one Nb atom and neighboring eight S atoms form a [NbS$_8$] hexahedron unit. Furthermore, $I4/mmm$-NbS$_2$ exhibits a higher superconducting critical temperature than 2$H$-NbS$_2$, as is resulted from the stronger electron-phonon coupling coefficients

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.