Stabilization of high-Tc phase of BiS2-based superconductor LaO0.5F0.5BiS2 using high-pressure synthesis

Abstract

High-quality polycrystalline samples of LaO0.5F0.5BiS2 were obtained using high-pressure synthesis technique. The LaO0.5F0.5BiS2 sample prepared by heating at 700 C under 2 GPa showed superconductivity with superconducting transition temperatures (Tc) of Tconset = 11.1 and Tczero = 8.5 K in the electrical resistivity measurements and Tconset = 11.5 and Tcirr = 9.4 K in the magnetic susceptibility measurements, which are obviously higher than those of the LaO0.5F0.5BiS2 polycrystalline samples obtained using conventional solid-state reaction. It was found that the high-Tc phase can be stabilized under high pressure and relatively-low annealing temperature. X-ray diffraction analysis revealed that the high-Tc phase possessed a small ratio of lattice constants of a and c, c/a.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.