Pressure effects on the superconductivity of HfPd2Al Heusler compound: Experimental and theoretical study

Abstract

Polycrystalline HfPd2Al has been synthesized using the arc-melting method and studied under ambient pressure conditions by x-ray diffraction from room temperature up to 450^oC. High pressure x-ray diffraction up to 23 GPa was also performed using Diacell-type membrane diamond anvil cells. The estimated linear thermal expansion coefficient was found to be α = 1.40(3)x10^{-5} K^{-1}, and the bulk modulus derived from the fit to the 3rd order Birch-Murnaghan EOS (BMEOS) is B0 = 97(2) GPa. Resistivity studies under applied pressure (p < 7.49 GPa) showed a linear decrease of superconducting critical temperature with increasing pressure and the slope dTc/dp = -0.13(1) K GPa^{-1}. The same behavior is observed for the electron-phonon coupling constant {λ_{ep}}(p) that changes from 0.67 to 0.6, estimated for p = 0.05 GPa and 7.49 GPa, respectively. First principles electronic structure and phonon calculation results are presented and used to estimate the magnitude of electron-phonon interaction {λ_{ep}} and its evolution with pressure. Theoretical results explain the experimentally observed decrease in Tc due to considerable lattice stiffening.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.