Hydrogen-substituted superconductors SmFeAsO1-xHx misidentified as oxygen-deficient SmFeAsO1-x

Abstract

We investigated the preferred electron dopants at the oxygen sites of 1111-type SmFeAsO by changing the atmospheres around the precursor with the composition of Sm:Fe:As:O = 1:1:1:1-x in high-pressure synthesis. Under H2O and H2 atmospheres, hydrogens derived from H2O or H2 molecules were introduced into the oxygen sites as a hydride ion, and SmFeAsO1-xHx was obtained. However, when the H2O and H2 sources were removed from the synthetic process, nearly stoichiometric SmFeAsO was obtained and the maximum amount of oxygen vacancies introduced remained x = 0.05(4). Density functional theory calculations indicated that substitution of hydrogen in the form of H- is more stable than the formation of an oxygen vacancy at the oxygen site of SmFeAsO. These results strongly imply that oxygen-deficient SmFeAsO1-x reported previously is SmFeAsO1-xHx with hydride ion incorporated unintentionally during high-pressure synthesis.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.