High pressure crystal growth of the antiperovskite centrosymmetric superconductor SrPt3P

Abstract

Bulk single crystals of SrPt3P have been grown for the first time by a self-flux method at 2 GPa and 1500 °C using the cubic-anvil, high-pressure and high-temperature technique. The grown black crystals were found to have either a plate-like or pillar-like morphology with maximum dimensions of ~ 1 - 0.6 - 0.3 mm3. According to a goniometric study the crystals are elongated in the ab-plane with the c-axis perpendicular to the plane. The crystal structure was confirmed by X-ray diffraction (P4/nmm, # 129, Z = 2, a = b = 5.7927(2) Å, c = 5.3729(2) Å and V = 180.290(11) Å3). Temperature dependent susceptibility measurements showed a single-phase behaviour and a superconducting transition temperature of 8.6 K. This value for single crystals is slightly higher than that previously reported for polycrystalline SrPt3P. The sharpness of the susceptibility drop (ΔTc = 0.07 K) supports a high homogeneity of obtained crystals.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.