Phase-separation control of K$_x$Fe$_{2-y}$Se$_2$ superconductor through rapid-quenching process

Abstract

K$_x$Fe$_{2-y}$Se$_2$ exhibits an iron-vacancy ordering at $T_{\rm s} {\sim}270°$C and separates into two phases: a minor superconducting (iron-vacancy-disordered) phase and a major non-superconducting (iron-vacancy-ordered) phase. The microstructural and superconducting properties of this intermixture can be tuned by an appropriate control of the quenching process through $T_{\rm s}$. A faster quenching rate leads to a finer microstructure and a suppression of formation of the non-superconducting phase by up to 50%. Nevertheless, such a faster cooling rate does induce a monotonic reduction in the superconducting transition temperature (from 30.7 K down to 26.0 K) and, simultaneously, a decrease in the iron content within the superconducting phase such that the compositional ratio changed from K$_{0.35}$Fe$_{1.83}$Se$_2$ to K$_{0.58}$Fe$_{1.71}$Se$_2$.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.