Modeling of internal mechanical failure of all-solid-state batteries during electrochemical cycling, and implications for battery design

Abstract

This is the first quantitative analysis of mechanical reliability of all-solid state batteries. Mechanical degradation of the solid electrolyte (SE) is caused by intercalation-induced expansion of the electrode particles, within the constrain of a dense microstructure. A coupled electro-chemo-mechanical model was implemented to quantify the material properties that cause a SE to fracture. The treatment of microstructural details is essential to the understanding of stress-localization phenomena and fracture. A cohesive zone model is employed to simulate the evolution of damage. In the numerical tests, fracture is prevented only if electrode-particle's expansion is lower than 7.5% and the solid-electrolyte's fracture energy higher than $G_c = 4$ J m$^{-2}$. Perhaps counter-intuitively, the analyses show that compliant solid electrolytes (with Young's modulus in the order of E$_{SE} = 15$ GPa) are more prone to micro-cracking. This result, captured by our non-linear kinematics model, contradicts the speculations that sulfide SEs are more suitable for the design of bulk-type batteries than oxide SEs. Mechanical degradation is linked to the battery power-density. Fracture in solid Li-ion conductors represents a barrier for Li transport, and accelerates the decay of rate performance.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.