Effect of mixed pinning landscapes produced by 6 MeV Oxygen irradiation on the resulting critical current densities J$_c$ in 1.3 $μ$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductors grown by co-evaporation

Abstract

We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$_c$ and flux creep rates in 1.3 $μ$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductor produced by co-evaporation. Pristine films with pinning produced mainly by random nanoparticles with diameter close to 50 nm were irradiated with doses between 2x10$^{13}$ cm$^{-2}$ and 4x10$^{14}$ cm$^{-2}$. At temperatures below 40 K with the magnetic field applied parallel (H//c) and at 45° (H//45°) to the c-axis, the in-field J$_c$ dependences can be significantly improved by irradiation. For doses of 1x10$^{14}$ cm$^{-2}$ the J$_c$ values at $μ$$_0$H = 5 T are doubled without affecting significantly the J$_c$ at small fields. Analyzing the flux creep rates as function of the temperature in both magnetic field configurations, it can be observed that the irradiation suppresses the peak associated with double-kink relaxation and increases the flux creep rates at intermediate and high temperatures. Under 0.5 T, the flux relaxation for H//c and H//45° in pristine films presents characteristic glassy exponents $μ$ = 1.63 and $μ$ = 1.45, respectively. For samples irradiated with 1x10$^{14}$ cm$^{-2}$, these values drop to $μ$ = 1.45 and $μ$ =1.24, respectively.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.