Dense superconducting phases of copper-bismuth at high pressure

Abstract

Although copper and bismuth do not form any compounds at ambient conditions, two intermetallics, CuBi and Cu$_{11}$Bi$_7$, were recently synthesized at high pressures. Here we report on the discovery of additional copper-bismuth phases at elevated pressures with high-densities from ab initio calculations. In particular, a Cu$_2$Bi compound is found to be thermodynamically stable at pressures above 59 GPa, crystallizing in the cubic Laves structure. In strong contrast to Cu$_{11}$Bi$_7$ and CuBi, cubic Cu$_2$Bi does not exhibit any voids or channels. Since the bismuth lone pairs in cubic Cu$_2$Bi are stereochemically inactive, the constituent elements can be closely packed and a high density of 10.52 g/cm$^{3}$ at 0 GPa is achieved. The moderate electron-phonon coupling of $λ=0.68$ leads to a superconducting temperature of 2 K, which exceeds the values observed both in Cu$_{11}$Bi$_7$and CuBi, as well as in elemental Cu and Bi .

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.