Actinium hydrides $AcH_{10}$, $AcH_{12}$, $AcH_{16}$ as high-temperature conventional superconductors

Abstract

Stability of numerous unexpected actinium hydrides was predicted via evolutionary algorithm USPEX. Electron-phonon interaction was investigated for the hydrogen-richest and most symmetric phases: R$\overline{3}$m-$AcH_{10}$, I4/mmm-$AcH_{12}$ and P$\overline{6}$m2-$AcH_{16}$. Predicted structures of actinium hydrides are consistent with all previously studied Ac-H phases and demonstrate phonon-mediated high-temperature superconductivity with Tc in the range 204-251 K for R$\overline{3}$m-$AcH_{10}$ at 200 GPa and 199-241 K for P$\overline{6}$m2-$AcH_{16}$ at 150 GPa which was estimated by directly solving of Eliashberg equation. Actinium belongs to the series of d1-elements (Sc-Y-La-Ac) that form high-Tc superconducting (HTSC) hydrides. Combining this observation with p0-HTSC hydrides ($MgH_{6}$ and $CaH_{6}$), we propose that p0- and d1-atoms with low-lying empty orbitals tend to form phonon-mediated HTSC metal polyhydrides.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.