Pressure-induced superconductivity in layered pnictogen diselenide NdO$_{0.8}$F$_{0.2}$Sb$_{1-x}$Bi$_x$Se$_2$ (x = 0.3 and 0.7)

Abstract

Polycrystalline samples of layered pnictogen diselenide NdO0.8F0.2Sb1-xBixSe2 (x = 0 to 0.8) were successfully synthesized by solid-state reactions. Electrical resistivity in the synthesized samples was systematically decreased with an increase in Bi content x. Crystal structure analysis using synchrotron X-ray diffraction suggests that insulator to metal transition upon Bi doping correlates with anomalous change in c-axis length and/or corrugation in conducting layer. The emergence of superconductivity under high pressure is demonstrated using diamond anvil cell (DAC) with boron-doped diamond electrodes, for x = 0.3 and 0.7 as the representative samples. For Sb-rich one (x = 0.3), we observed a superconducting transition with Tconset = 5.3 K at 50 GPa, which is the first-ever report of the superconductivity in layered SbCh2-based (Ch: chalcogen) compounds. The Tconset of x = 0.3 increased with increasing pressure and reached 7.9 K at 70.8 GPa, followed by the gradual decrease in Tc up to 90 GPa. For Bi-rich one (x = 0.7), a superconducting transition with Tconset = 5.9 K was observed at 43.5 GPa, which is the almost comparable to that of x = 0.3; besides, upper critical field (Hc2) is evaluated to be ~10 T for x = 0.7, which is higher than that of x = 0.3 (Hc2 = 6.7 T at 50 GPa).

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.