First performance test of 30 mm iron-based superconductor single pancake coil under 24 T background field

Abstract

The iron-based superconductor (IBS) single pancake coil (SPC) with 30 mm inner diameter was firstly fabricated and tested under 24 T background field. This SPC was successfully made using the 7-filamentary Ba1-xKxFe2As2 (Ba122) tape by wind-and-react method. This IBS coil show the highest Ic value at magnetic field reported so far. For example, the transport critical current of this Ba122 SPC achieved 35 A at 4.2 K and 10 T, which is about half of that of short sample. This indicates that the non-insulation winding process together with the stainless-steel tape is suitable to the iron-based superconductor. Even more encouraging is the fact that the Ic of this SPC is still as high as 26 A under 24 T background field, which is still about 40% of that at zero external magnetic field. These results clearly demonstrate that the iron-based superconductors are very promising for high-field magnet applications.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.