Efficient indoor p-i-n hybrid perovskite solar cells using low temperature solution processed NiO as hole extraction layers

Abstract

Hybrid perovskites have received tremendous attention due to their exceptional photovoltaic and optoelectronic properties. Among the two widely used perovskite solar cell device architectures of n-ip and p-i-n, the latter is interesting in terms of its simplicity of fabrication and lower energy input. However this structure mostly uses PEDOT:PSS as a hole transporting layer which can accelerate the perovskite solar cell degradation. Hence the development of stable, inorganic hole extraction layers (HEL), without compromising the simplicity of device fabrication is crucial in this fast-growing photovoltaic field. Here we demonstrate a low temperature (~100 oC) solution - processed and ultrathin (~ 6 nm) NiO nanoparticle thin films as an efficient HEL for CH3NH3PbI3 based perovskite solar cells. We measure a power conversion efficiency (PCE) of 13.3 % on rigid glass substrates and 8.5 % on flexible substrates. A comparison with PEDOT:PSS based MAPbI3 solar cells (PCE ~ 7.9 %) shows that NiO based solar cells have higher short circuit current density and improved open circuit voltage (1.03V). Apart from the photovoltaic performance under 1 Sun, the efficient hole extraction property of NiO is demonstrated for indoor lighting as well with a PCE of 23.0 % for NiO based CH3NH3PbI2.9Cl0.1 p-i-n solar cells under compact fluorescent lighting. Compared to the perovskite solar cells fabricated on PEDOT:PSS HEL, better shelf-life stability is observed for perovskite solar cells fabricated on NiO HEL. Detailed microstructural and photophysical investigations imply uniform morphology, lower recombination losses, and improved charge transfer properties for CH3NH3PbI3 grown on NiO HEL.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.