Aspects of the synthesis of thin film superconducting infinite-layer nickelates

Abstract

The recent observation of superconductivity in Nd$_{0.8}$Sr$_{0.2}$NiO$_{2}$ calls for further investigation and optimization of the synthesis of this metastable infinite-layer nickelate structure. Here, we present our current understanding of important aspects of the growth of the parent perovskite compound via pulsed laser deposition on SrTiO$_{3}$ (001) substrates, and the subsequent topotactic reduction. We find that to achieve single-crystalline, single-phase superconducting Nd$_{0.8}$Sr$_{0.2}$NiO$_{2}$, it is essential that the precursor perovskite Nd$_{0.8}$Sr$_{0.2}$NiO$_{3}$ thin film is stabilized with high crystallinity and no impurity phases; in particular, a Ruddlesden-Popper-type secondary phase is often observed. We have further investigated the evolution of the soft-chemistry topotactic reduction conditions to realize full transformation to the infinite-layer structure with no film decomposition or formation of other phases. We find that capping the nickelate film with a subsequent SrTiO$_{3}$ layer provides an epitaxial template to the top region of the nickelate film, much like the substrate. Thus, for currently optimized growth conditions, we can stabilize superconducting single-phase Nd$_{0.8}$Sr$_{0.2}$NiO$_{2}$ (001) epitaxial thin films up to ~ 10 nm.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.