Stabilization mechanism of clathrate H cages in a room-temperature superconductor LaH$_{10}$

Abstract

Lanthanum hydride LaH$_{10}$ with a sodalitelike clathrate structure was experimentally realized to exhibit a room-temperature superconductivity under megabar pressures. Based on first-principles calculations, we reveal that the metal framework of La atoms has the excess electrons at interstitial regions. Such anionic electrons are easily captured to form a stable clathrate structure of H cages. We thus propose that the charge transfer from La to H atoms is mostly driven by the electride property of the La framework. Further, the interaction between La atoms and H cages induces a delocalization of La-5$p$ semicore states to hybridize with H-1$s$ state. Consequently, the bonding nature between La atoms and H cages is characterized as a mixture of ionic and covalent. Our findings demonstrate that anionic and semicore electrons play important roles in stabilizing clathrate H cages in LaH$_{10}$, which can be broadly applicable to other high-pressure rare-earth hydrides with clathrate structures.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.