Experimental evidence for orthorhombic Fddd crystal structure in elemental yttrium above 100 GPa

Abstract

We present electrical resistance measurements of elemental yttrium on bulk and film samples, and both exhibit superconductivity at very high pressures. We show that the pressure dependence of the superconducting transition temperature above 100 GPa is in good agreement with the predicted Fddd phase by Chen et al. [Phys. Rev. lett. 109, 157004 (2012)]. This result together with a new Rietveld refinement made on X-ray data at 123 GPa from Samudrala et al. [J. Phys. Condens. Matter 24, 362201 (2012)] offer strong evidence that the atomic structure of yttrium above 100 GPa is orthorhombic Fddd. Furthermore, our process of evaporating yttrium film directly on a diamond anvil is expected to be a valuable asset for future synthesis of new superhydride superconductors.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.