Spectroscopic Evidence for the Superconductivity of Elemental Metal Y under Pressure

Abstract

Very high applied pressure induces superconductivity with the transition temperature ($T_c$) exceeding 19 K in elemental yttrium, but relatively little is known about the nature of that superconductivity. From point-contact spectroscopy (PCS) measurements in a diamond anvil cell (DAC), a strong enhancement in the differential conductance is revealed near the zero-biased voltage owing to Andreev reflection, a hallmark of the superconducting (SC) phase. Analysis of the PCS spectra based on the extended Blonder-Tinkham-Klapwijk (BTK) model indicates two SC gaps at 48.6 GPa, where the large gap $Δ_L$ is 3.63 meV and the small gap $Δ_S$ is 0.46 meV. When scaled against a reduced temperature, both small and large SC gaps collapse on a single curve that follows the prediction from BCS theory. The SC gap-to-$T_c$ ratio is 8.2 for the larger gap, and the initial slope of the upper critical field is -1.9 T/K, indicating that Y belongs to a family of strongly coupled BCS superconductors. The successful application of PCS to Y in DAC environments demonstrates its utility for future research on other pressure-induced high-$T_c$ superconductors.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.