High-$T_c$ superconducting hydrides formed by LaH$_{24}$ and YH$_{24}$ cage structures as basic blocks

Abstract

Based on recent studies regarding high-temperature (high-$T_c$) La-Y ternary hydrides (e.g., $P{\bar{1}}$-La$_2$YH$_{12}$, $Pm{\bar{3}}m$-LaYH$_{12}$, and $Pm{\bar{3}}m$-(La,Y)H$_{10}$ with a maximum $T_c \sim 253$ K), we examined the phase and structural stabilities of the (LaH$_6$)(YH$_6$)$_y$ series as high-$T_c$ ternary hydride compositions using a genetic algorithm and $\it ab$ $\it initio$ calculations. Our evaluation showed that the $Pm\bar{3}m$-LaYH$_{12}$ reported in the previous study was unstable during decomposition into $R\bar{3}c$-LaH$_{6}$ + $Im\bar{3}m$-YH$_{6}$. We also discovered new crystal structures, namely $Cmmm$-LaYH$_{12}$ ($y=1$), $R\bar{3}c$-LaYH$_{12}$ ($y=1$), $Cmmm$-LaY$_3$H$_{24}$ ($y=3$), and $R\bar{3}$-LaY$_3$H$_{24}$ ($y=3$), showing stability against such decomposition. While $R\bar{3}c$ ($y=1$) and $R\bar{3}$ ($y=3$) did not exhibit superconductivity owing to the extremely low density of states at the Fermi level, $Cmmm$ phases exhibited a $T_{c}$ of approximately 140~K at around 200~GPa owing to the extremely high electron--phonon coupling constant ($λ$ = 1.876 for LaYH$_{12}$). By the twice longer stacking for $Cmmm$-LaY$_3$H$_{24}$, the coupling constant increased owing to the chemical pressure of Y, leading to a slightly increased $T_{c}$.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.