Design Principles for High Temperature Superconductors with Hydrogen-based Alloy Backbone at Moderate Pressure

Abstract

Hydrogen-based superconductors provide a route to the long-sought goal of room-temperature superconductivity, but the high pressures required to metallize these materials limit their immediate application. For example, carbonaceous sulfur hydride, the first room-temperature superconductor, can reach a critical temperature (Tc) of 288 K only at the extreme pressure of 267 GPa. The next recognized challenge is the realization of room-temperature superconductivity at significantly lower pressures. Here, we propose a strategy for the rational design of high-temperature superconductors at low pressures by alloying small-radius elements and hydrogen to form ternary hydride superconductors with alloy backbones. We identify a hitherto unknown fluorite-type backbone in compositions of the form AXH8, which exhibit high temperature superconductivity at moderate pressures. The Fm-3m phase of LaBeH8, with a fluorite-type H-Be alloy backbone, is predicted to be metastable and superconducting with a Tc ~ 191 K at 50 GPa; a substantially lower pressure than that required by the geometrically similar clathrate hydride LaH10 (170 GPa). Our approach paves the way for finding high-Tc ternary hydride superconductors at conditions close to ambient pressures.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.