Structural Diversity and Superconductivity in S-P-H Ternary Hydrides Under Pressure

Abstract

Evolutionary structure searches revealed a plethora of stable and low-enthalpy metastable phases in the S-P-H ternary phase diagram under pressure. A wide variety of crystalline structure types were uncovered ranging from those possessing one-dimensional chains, two-dimensional sheets based on S-H or S-P-H square lattices as well as S-H or P-H honeycombs, and cage-like structures. Some of the cage-like structures could be derived from doping the high-pressure high-temperature superconducting $Im\bar{3}m$ H$_3$S phase with phosphorous. Most of the discovered compounds were metallic, however those derived from $Im\bar{3}m$ H$_3$S lattices with low levels of P-doping were predicted to possess the highest superconducting critical temperatures ($T_c$s). The propensity for phosphorous to assume octahedral coordination, as well as the similar radii of sulfur and phosphorous are key to maintaining a high density of states at the Fermi level in $Im\bar{3}m$ S$_{0.875}$P$_{0.125}$H$_3$, whose $T_c$ was estimated to be similar to that of H$_3$S at 200~GPa.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.