Synthesis and Superconductivity in yttrium superhydrides under high pressure

Abstract

The flourishing rare earth superhydrides are a class of recently discovered materials that possess near-room-temperature superconductivity at high pressures, opening a new era of superconductivity research at high pressures. Among these superhydrides, yttrium superhydrides attracted great interest owing to their abundance of stoichiometries and excellent superconductivities. Here, we carried out a comprehensive study of yttrium superhydrides in a wide pressure range of 145-300 GPa. We successfully synthesized a series of superhydrides with the compositions of YH4, YH6, YH7, and YH9, and reported their superconducting transition temperatures of 82 K at 167 GPa, 218 K at 165 GPa, 29 K at 162 GPa, and 230 K at 300 GPa, respectively, which were evidenced by a sharp drop of resistivity. The structure and superconductivity of YH4, which was taken as a representative example, were also examined by X-ray diffraction measurements and the suppression of the superconductivity under external magnetic fields, respectively. Clathrate YH10 as a candidate of room-temperature superconductor was not synthesized within the studied pressure and temperature ranges of up to 300 GPa and 2000 K, respectively. The current work created a detailed platform for further searching room-temperature superconductors in polynary yttrium-based superhydrides.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.