Synthesis of Superconducting Phase of La$_{0.5}$Ce$_{0.5}$H$_{10}$ at High Pressures

Abstract

Clathrate hydride \emph{Fm}\={3}\emph{m}-LaH$_{10}$ has been proven as the most extraordinary superconductor with the critical temperature $T_c$ above 250 K upon compression of hundreds of GPa in recent years. A general hope is to reduce the stabilization pressure and maintain the high $T_c$ value of the specific phase in LaH$_{10}$. However, strong structural instability distorts \emph{Fm}\={3}\emph{m} structure and leads to a rapid decrease of $T_c$ at low pressures. Here, we investigate the phase stability and superconducting behaviors of \emph{Fm}\={3}\emph{m}-LaH$_{10}$ with enhanced chemical pre-compression through partly replacing La by Ce atoms from both experiments and calculations. For explicitly characterizing the synthesized hydride, we choose lanthanum-cerium alloy with stoichiometry composition of 1:1. X-ray diffraction and Raman scattering measurements reveal the stabilization of \emph{Fm}\={3}\emph{m}-La$_{0.5}$Ce$_{0.5}$H$_{10}$ in the pressure range of 140-160 GPa. Superconductivity with $T_c$ of 175$\pm$2 K at 155 GPa is confirmed with the observation of the zero-resistivity state and supported by the theoretical calculations. These findings provide applicability in the future explorations for a large variety of hydrogen-rich hydrides.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.