Observation of Conventional Near Room Temperature Superconductivity in Carbonaceous Sulfur Hydride

Abstract

The phenomenon of high temperature superconductivity, approaching room temperature, has been realized in a number of hydrogen-dominant alloy systems under high pressure conditions1-12. A significant discovery in reaching room temperature superconductivity is the photo-induced reaction of sulfur, hydrogen, and carbon that initially forms of van der Waals solids at sub-megabar pressures. Carbonaceous sulfur hydride has been demonstrated to be tunable with respect to carbon content, leading to different superconducting final states with different structural symmetries. A modulated AC susceptibility technique adapted for a diamond anvil cell confirms a Tc of 260 kelvin at 133 GPa in carbonaceous sulfur hydride. Furthermore, direct synchrotron infrared reflectivity measurements on the same sample under the same conditions reveal a superconducting gap of ~85 meV at 100 K in close agreement to the expected value from Bardeen-Cooper-Schrieffer (BCS) theory13-18. Additionally, x-ray diffraction in tandem with AC magnetic susceptibility measurements above and below the superconducting transition temperature, and as a function of pressure at 107-133 GPa, reveal the Pnma structure of the material is responsible for the close to room-temperature superconductivity at these pressures.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.