Crystal structures and high-temperature superconductivity in molybdenum-hydrogen binary system under high pressure

Abstract

Motivated by advances in hydrogen-rich superconductors in the past decades, we conducted variable-composition structural searches in Mo-H binary system at high pressure. A new composition-pressure phase diagram of thermodynamically stable structures has been derived. Besides all previously discovered superconducting molybdenum hydrides, we also identified series of thermodynamically metastable superconducting structures, including I4/mmm-Mo$_3$H$_{14}$, I4cm-MoH$_9$, P4/nmm-MoH$_{10}$ and P42$_1$2-MoH$_{10}$, with the superconducting transition temperatures from 55 to 126 K at 300 GPa. In these superconducting molybdenum hydrides, vibrations of the Mo-atoms contributes significantly to the electron-phonon coupling and the superconducting transition temperature, in complementary to the contributions by the vibrations of the H-atoms. Our works highlight the importance of compounds with non-integer composition ratio and metastable states in material searches, for example the potential high temperature superconductors.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.