Absence of Tc-Pinning Phenomenon Under High Pressure in High-Entropy REO0.5F0.5BiS2 Layered Superconductor

Abstract

Recently, robustness of superconductivity (transition temperature, Tc) under high pressures has been observed in high-entropy alloy (HEA), bcc-type Ti-Zr-Hf-Nb-Ta, and HEA-type compounds (Ag,In,Sn,Pb,Bi)Te with a NaCl-type structure. Since those materials have three-dimensional crystal structure, investigation on the pressure dependence of Tc of low-dimensional materials is needed to understand the phenomena. Here, we investigated the superconducting properties and the crystal structure of BiS2-based layered system REO0.5F0.5BiS2. Although the robustness of Tc was induced in MTe with increasing M-site configurational entropy, the increase in RE-site configurational entropy does not induce robustness of Tc under high pressures in REO0.5F0.5BiS2. The crystal structure of HEA-type REO0.5F0.5BiS2 was confirmed as monoclinic P21/m, which is the same space group as the zero-entropy counterpart LaO0.5F0.5BiS2. The results suggest that an increase in configurational entropy at blocking layers do not affect crystal structure and superconducting properties under high pressures in the BiS2-based layered system.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.