Structural transitions, octahedral rotations, and electronic properties of A3Ni2O7 rare-earth nickelates under high pressure

Abstract

Motivated by the recent observation of superconductivity with $T_c \sim 80$ K in pressurized La3Ni2O7 [Nature 621, 493 (2023)], we explore the structural and electronic properties in A3Ni2O7 bilayer nickelates (A=La-Lu, Y, Sc) as a function of hydrostatic pressure (0-150 GPa) from first principles including a Coulomb repulsion term. At $\sim 20$ GPa, we observe an orthorhombic-to-tetragonal transition in La$_3$Ni$_2$O$_7$ at variance with recent x-ray diffraction data, which points to so-far unresolved complexities at the onset of superconductivity, e.g., charge doping by variations in the oxygen stoichiometry. We compile a structural phase diagram with particular emphasis on the $b/a$ ratio, octahedral anisotropy, and octahedral rotations. Intriguingly, chemical and external pressure emerge as two distinct and counteracting control parameters. We find unexpected correlations between $T_c$ and the in-plane Ni-O-Ni bond angles for La$_3$Ni$_2$O$_7$. Moreover, two novel structural phases with significant $c^+$ octahedral rotations and in-plane bond disproportionations are uncovered for A=Nd-Lu, Y, Sc that exhibit a surprising pressure-driven electronic reconstruction in the Ni $e_g$ manifold. By disentangling the involvement of basal versus apical oxygen states at the Fermi surface, we identify Tb$_3$Ni$_2$O$_7$ as an interesting candidate for superconductivity at ambient pressure. These results suggest a profound tunability of the structural and electronic phases in this novel materials class and are key for a fundamental understanding of the superconductivity mechanism.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.