Measurements of the first-flux-penetration field in surface-treated and coated Nb: Distinguishing between surface pinning and an interface energy barrier

Abstract

We report measurements of the first-flux-penetration field in surface-treated and coated Nb samples using muon spin rotation ($μ$SR). Using thin Ag foils as energy moderators for the implanted muon spin-probes, we "profile" the vortex penetration field $μ_{0} H_{\mathrm{vp}}$ at sub-surface depths on the order of $\sim 10$ $\mathrmμ$m to $\sim 100$ $\mathrmμ$m. In a coated sample [Nb$_3$Sn(2 $\mathrmμ$m)/Nb], we find that $μ_{0} H_{\mathrm{vp}}$ is depth-independent with a value of 234.5(35) mT, consistent with Nb's metastable superheating field and suggestive of surface energy barrier for flux penetration. Conversely, in a surface-treated sample [Nb baked in vacuum at 120 $^{\circ}$C for 48 h], vortex penetration onsets close to pure Nb's lower critical field $μ_{0}H_\mathrm{c1} \approx 170$ mT, but increases with increasing implantation depth, consistent with flux-pinning localized at the surface. The implication of these results for technical applications of superconducting Nb, such as superconducting radio frequency (SRF) cavities, is discussed.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.