Ac$_3$Ni$_2$O$_7$ and La$_2$$Ae$Ni$_2$O$_6$F ($Ae$ = Sr, Ba): Benchmark Materials for Bilayer Nickelate Superconductivity

Abstract

We theoretically propose Ac$_3$Ni$_2$O$_7$, La$_2$BaNi$_2$O$_6$F, and La$_2$SrNi$_2$O$_6$F compounds to be benchmark materials for bilayer nickelate superconductivity. The stable phase of Ac$_3$Ni$_2$O$_7$ and La$_2$BaNi$_2$O$_6$F are found to be $I4/mmm$ without the lattice distortion caused by octahedra rotation at ambient pressure, where as the lattice distortion in La$_2$SrNi$_2$O$_6$F can be suppressed with relatively small external pressure of 4 GPa. The magnetism, electronic structure and spin susceptibilities of Ac$_3$Ni$_2$O$_7$ are extremely close to those of La$_3$Ni$_2$O$_7$ at 30 GPa. The ground state of La$_2$BaNi$_2$O$_6$F and La$_2$SrNi$_2$O$_6$F are antiferromagnetically coupled checkerboard bilayer with sizable magnetic moment on Ni. In addition, the inter-layer coupling $J_{\perp}$ between Ni-bilayers in La$_2$BaNi$_2$O$_6$F or La$_2$SrNi$_2$O$_6$F is only $\sim$ 1/10 of that in Ac$_3$Ni$_2$O$_7$ or La$_3$Ni$_2$O$_7$ at 30 GPa. We argue that these compounds may serve as superconducting candidates at ambient pressure and can be employed to testify theoretical proposals for bilayer nickelate superconductivity.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.